IS 1570 (Part 5) X02Cr19Ni10 vs EN 10088-1 X2CrNi18-9

Strong Match — 91% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X02Cr19Ni10 (IS 1570 (Part 5):1985) and EN 10088-1 X2CrNi18-9 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrNi18-9 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X02Cr19Ni10 vs EN 10088-1 X2CrNi18-9 is a 91% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91%.

Frequently Compared With IS 1570 (Part 5) X02Cr19Ni10:
EN 10088-1 1.4845 ASTM A959 201L EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 ASTM A959 .- GOST 5632 12Kh13 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
91%
MECHANICAL MATCH
No shared data
OVERALL
91%
Specifications
Property IS 1570 (Part 5) X02Cr19Ni10 EN 10088-1 X2CrNi18-9
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Cr (%) 17.5-20.0 17.5-19.5
Ni (%) 8.0-12.0 8.0-10.5
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X02Cr19Ni10 EN 10088-1 X2CrNi18-9
Tensile Strength >=485 MPa Not specified
Yield Strength >=170 MPa (0.2 % proof stress) Not specified
Elongation >=40% (50 mm) Not specified
Hardness <=183 HB; <=88 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Key Differences
Can IS 1570 (Part 5) X02Cr19Ni10 Be Substituted With EN 10088-1 X2CrNi18-9?
IS 1570 (Part 5) X02Cr19Ni10 and EN 10088-1 X2CrNi18-9 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNi18-9 is often considered as a substitute for IS 1570 (Part 5) X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X02Cr19Ni10
0 active listings and RFQs →
EN 10088-1 X2CrNi18-9
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X02Cr19Ni10 and EN 10088-1 X2CrNi18-9?
EN 10088-1 X2CrNi18-9 specifies N which is not specified for IS 1570 (Part 5) X02Cr19Ni10.
Can IS 1570 (Part 5) X02Cr19Ni10 be substituted with EN 10088-1 X2CrNi18-9?
IS 1570 (Part 5) X02Cr19Ni10 and EN 10088-1 X2CrNi18-9 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNi18-9 is often considered as a substitute for IS 1570 (Part 5) X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.