Post Stock Login Register

JIS G4303 SUS316 vs ASTM A959 316LHN

Close Alternative — 76.9% match based on chemical composition and mechanical property overlap.

JIS G4303 SUS316 (JIS G4303:2021) and ASTM A959 316LHN (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4303 SUS316 is typically used for marine applications, chemical processing, pharmaceutical equipment, while ASTM A959 316LHN is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4303 SUS316 is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 316LHN is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4303 SUS316 vs ASTM A959 316LHN is a 76.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.9%.

Frequently Compared With JIS G4303 SUS316:
EN 10088-1 1.4401 GOST 5632 08X18H10 GOST 5632 12Kh13 EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4845 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
76.9%
MECHANICAL MATCH
No shared data
OVERALL
76.9%
Specifications
Property JIS G4303 SUS316 ASTM A959 316LHN
Standard JIS G4303:2021 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) ≤0.08 <=0.03
Si (%) ≤1.00 <=1.00
Mn (%) ≤2.00 <=2.00
Cr (%) 16.0–18.0 16.0-18.0
Ni (%) 10.0–14.0 10.0-13.0
Mo (%) 2.0–3.0 2.00-3.00
N (%) Not specified 0.16-0.30
P (%) Not specified <=0.045
S (%) Not specified <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4303 SUS316 ASTM A959 316LHN
Tensile Strength ≥520 MPa Not specified
Yield Strength ≥205 MPa Not specified
Elongation ≥40% Not specified
Hardness ≤187 HB Not specified
Typical Applications
JIS G4303 SUS316
Marine applications, chemical processing, pharmaceutical equipment
ASTM A959 316LHN
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4303 SUS316 Be Substituted With ASTM A959 316LHN?
JIS G4303 SUS316 and ASTM A959 316LHN are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
JIS G4303 SUS316
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2800–3300 mm (110.24–129.92 in)
ASTM A959 316LHN
No active listings currently.
On M-EX Right Now
JIS G4303 SUS316
3 active listings and RFQs →
ASTM A959 316LHN
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4303 SUS316 and ASTM A959 316LHN?
ASTM A959 316LHN specifies N, P, S which are not specified for JIS G4303 SUS316.
Can JIS G4303 SUS316 be substituted with ASTM A959 316LHN?
JIS G4303 SUS316 and ASTM A959 316LHN are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.