NF A35-574 Z7CN18-09 vs IS 1570 (Part 7) 12Cr12MoVH

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

NF A35-574 Z7CN18-09 (NF A35-574:1990) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. NF A35-574 Z7CN18-09 is typically used for used for food processing equipment, kitchen equipment, chemical tanks, piping, architectural components, and fasteners., while IS 1570 (Part 7) 12Cr12MoVH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. NF A35-574 Z7CN18-09 is defined under Association Francaise de Normalisation (NF), originating from France, while IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, NF A35-574 Z7CN18-09 vs IS 1570 (Part 7) 12Cr12MoVH is a 54.3% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With NF A35-574 Z7CN18-09:
GB/T 3280 06Cr19Ni10 GOST 5632 12Kh13 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 EN 10088-1 1.4401 EN 10088-1 1.4006 EN 10088-1 1.4301 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
54.3%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property NF A35-574 Z7CN18-09 IS 1570 (Part 7) 12Cr12MoVH
Standard NF A35-574:1990 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) 0.08 max 0.08-0.16
Si (%) 1.00 max <=0.60
Mn (%) 2.00 max 0.40-1.00
Cr (%) 17.00-19.00 11.5-13.00
Ni (%) 8.00-10.50 <=1.0
P (%) 0.045 max <=0.040
S (%) 0.030 max <=0.035
Mo (%) Not specified 0.40-0.80
V (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property NF A35-574 Z7CN18-09 IS 1570 (Part 7) 12Cr12MoVH
Tensile Strength 500-700 MPa 770-930 MPa
Yield Strength 190-250 MPa >=585 MPa (0.2 % proof stress)
Elongation 40-55% >=15%
Hardness 140-210 HB Not specified
Condition Not specified Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
NF A35-574 Z7CN18-09
Used for food processing equipment, kitchen equipment, chemical tanks, piping, architectural components, and fasteners.
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can NF A35-574 Z7CN18-09 Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
NF A35-574 Z7CN18-09 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
NF A35-574 Z7CN18-09
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2600–2900 mm (102.36–114.17 in)
IS 1570 (Part 7) 12Cr12MoVH
No active listings currently.
On M-EX Right Now
NF A35-574 Z7CN18-09
2 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between NF A35-574 Z7CN18-09 and IS 1570 (Part 7) 12Cr12MoVH?
IS 1570 (Part 7) 12Cr12MoVH specifies Mo, V which are not specified for NF A35-574 Z7CN18-09.
Can NF A35-574 Z7CN18-09 be substituted with IS 1570 (Part 7) 12Cr12MoVH?
NF A35-574 Z7CN18-09 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.