NF A35-574 Z7CN18-09 vs ASTM A959 .-

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

NF A35-574 Z7CN18-09 (NF A35-574:1990) and ASTM A959 .- (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. NF A35-574 Z7CN18-09 is typically used for used for food processing equipment, kitchen equipment, chemical tanks, piping, architectural components, and fasteners., while ASTM A959 .- is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). NF A35-574 Z7CN18-09 is defined under Association Francaise de Normalisation (NF), originating from France, while ASTM A959 .- is defined under ASTM International, originating from United States.

As per chemical composition, NF A35-574 Z7CN18-09 vs ASTM A959 .- is a 70% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With NF A35-574 Z7CN18-09:
GB/T 3280 06Cr19Ni10 GOST 5632 12Kh13 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 EN 10088-1 1.4401 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
70%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property NF A35-574 Z7CN18-09 ASTM A959 .-
Standard NF A35-574:1990 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.08 max <=0.030
Si (%) 1.00 max <=1.00
Mn (%) 2.00 max <=1.00
Cr (%) 17.00-19.00 18.0-20.0
Ni (%) 8.00-10.50 <=0.50
P (%) 0.045 max <=0.040
S (%) 0.030 max <=0.030
Cb (%) Not specified 0.10-0.60
N (%) Not specified <=0.030
Ti (%) Not specified 0.07-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property NF A35-574 Z7CN18-09 ASTM A959 .-
Tensile Strength 500-700 MPa Not specified
Yield Strength 190-250 MPa Not specified
Elongation 40-55% Not specified
Hardness 140-210 HB Not specified
Typical Applications
NF A35-574 Z7CN18-09
Used for food processing equipment, kitchen equipment, chemical tanks, piping, architectural components, and fasteners.
ASTM A959 .-
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can NF A35-574 Z7CN18-09 Be Substituted With ASTM A959 .-?
NF A35-574 Z7CN18-09 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
NF A35-574 Z7CN18-09
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2600–2900 mm (102.36–114.17 in)
ASTM A959 .-
No active listings currently.
On M-EX Right Now
NF A35-574 Z7CN18-09
2 active listings and RFQs →
ASTM A959 .-
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between NF A35-574 Z7CN18-09 and ASTM A959 .-?
ASTM A959 .- specifies Cb, N, Ti which are not specified for NF A35-574 Z7CN18-09.
Can NF A35-574 Z7CN18-09 be substituted with ASTM A959 .-?
NF A35-574 Z7CN18-09 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.