EN 10088-1 1.4006 vs GB/T 3280 06Cr19Ni10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-1 1.4006 (EN 10088-1:2014) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 1.4006 is typically used for cutlery, turbine blades, fasteners, surgical instruments, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, EN 10088-1 1.4006 vs GB/T 3280 06Cr19Ni10 is a 62.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-1 1.4006:
GOST 5632 12Kh13 GOST 5632 08X18H10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4845 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 202 IS 1570 (Part 7) 12Cr13H ASTM A959 2205 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
62.9%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10
Standard EN 10088-1:2014 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) 0.08–0.15 0.08 max
Si (%) ≤1.00 1.00 max
Mn (%) ≤1.50 2.00 max
Cr (%) 11.5–13.5 18.00-20.00
Ni (%) ≤0.75 8.00-11.00
P (%) Not specified 0.045 max
S (%) Not specified 0.030 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10
Tensile Strength ≥540 MPa (annealed) 520-720 MPa
Hardness HRC 36–45 (hardened) Not specified
Elongation ≥18% 40-60%
Yield Strength Not specified 205-310 MPa
Hardness Not specified 187 HB max
Typical Applications
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can EN 10088-1 1.4006 Be Substituted With GB/T 3280 06Cr19Ni10?
EN 10088-1 1.4006 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
EN 10088-1 1.4006
3 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 1.4006 and GB/T 3280 06Cr19Ni10?
GB/T 3280 06Cr19Ni10 specifies P, S which are not specified for EN 10088-1 1.4006.
Can EN 10088-1 1.4006 be substituted with GB/T 3280 06Cr19Ni10?
EN 10088-1 1.4006 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.