GB/T 3280 06Cr19Ni10 vs ASTM A959 16-8-2H

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) and ASTM A959 16-8-2H (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. GB/T 3280 06Cr19Ni10 is typically used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners., while ASTM A959 16-8-2H is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China, while ASTM A959 16-8-2H is defined under ASTM International, originating from United States.

As per chemical composition, GB/T 3280 06Cr19Ni10 vs ASTM A959 16-8-2H is a 72.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GB/T 3280 06Cr19Ni10:
EN 10088-1 1.4845 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13 IS 1570 (Part 7) 12Cr12MoH ASTM A959 202 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
72.7%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property GB/T 3280 06Cr19Ni10 ASTM A959 16-8-2H
Standard GB/T 3280-2015 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.08 max 0.05-0.10
Si (%) 1.00 max <=1.00
Mn (%) 2.00 max <=2.00
Cr (%) 18.00-20.00 14.5-16.5
Ni (%) 8.00-11.00 7.5-9.5
P (%) 0.045 max <=0.045
S (%) 0.030 max <=0.030
Mo (%) Not specified 1.50-2.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3280 06Cr19Ni10 ASTM A959 16-8-2H
Tensile Strength 520-720 MPa Not specified
Yield Strength 205-310 MPa Not specified
Elongation 40-60% Not specified
Hardness 187 HB max Not specified
Typical Applications
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
ASTM A959 16-8-2H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can GB/T 3280 06Cr19Ni10 Be Substituted With ASTM A959 16-8-2H?
GB/T 3280 06Cr19Ni10 and ASTM A959 16-8-2H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
ASTM A959 16-8-2H
No active listings currently.
On M-EX Right Now
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
ASTM A959 16-8-2H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3280 06Cr19Ni10 and ASTM A959 16-8-2H?
ASTM A959 16-8-2H specifies Mo which is not specified for GB/T 3280 06Cr19Ni10.
Can GB/T 3280 06Cr19Ni10 be substituted with ASTM A959 16-8-2H?
GB/T 3280 06Cr19Ni10 and ASTM A959 16-8-2H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.