GB/T 3280 06Cr19Ni10 vs IS 1570 (Part 7) 12Cr12MoH

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) and IS 1570 (Part 7) 12Cr12MoH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. GB/T 3280 06Cr19Ni10 is typically used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners., while IS 1570 (Part 7) 12Cr12MoH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China, while IS 1570 (Part 7) 12Cr12MoH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, GB/T 3280 06Cr19Ni10 vs IS 1570 (Part 7) 12Cr12MoH is a 59.9% match. As per mechanical properties, the match is 3.7%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GB/T 3280 06Cr19Ni10:
EN 10088-1 1.4845 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 ASTM A959 16-8-2H ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13 ASTM A959 202 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
59.9%
MECHANICAL MATCH
3.7%
OVERALL
35%
Specifications
Property GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoH
Standard GB/T 3280-2015 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) 0.08 max 0.08-0.16
Si (%) 1.00 max <=0.60
Mn (%) 2.00 max 0.40-1.00
Cr (%) 18.00-20.00 11.5-13.00
Ni (%) 8.00-11.00 <=1.0
P (%) 0.045 max <=0.040
S (%) 0.030 max <=0.035
Mo (%) Not specified 0.40-0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoH
Tensile Strength 520-720 MPa 680-880 MPa
Yield Strength 205-310 MPa >=490 MPa (0.2 % proof stress)
Elongation 40-60% >=20%
Hardness 187 HB max Not specified
Condition Not specified Bars, forgings, Q+T, thickness up to 75 (first row of Table 3)
Typical Applications
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
IS 1570 (Part 7) 12Cr12MoH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can GB/T 3280 06Cr19Ni10 Be Substituted With IS 1570 (Part 7) 12Cr12MoH?
GB/T 3280 06Cr19Ni10 and IS 1570 (Part 7) 12Cr12MoH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
IS 1570 (Part 7) 12Cr12MoH
No active listings currently.
On M-EX Right Now
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3280 06Cr19Ni10 and IS 1570 (Part 7) 12Cr12MoH?
IS 1570 (Part 7) 12Cr12MoH specifies Mo which is not specified for GB/T 3280 06Cr19Ni10.
Can GB/T 3280 06Cr19Ni10 be substituted with IS 1570 (Part 7) 12Cr12MoH?
GB/T 3280 06Cr19Ni10 and IS 1570 (Part 7) 12Cr12MoH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.