Minimal Match — 54.6% match
based on chemical composition and mechanical property overlap.
GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) and IS 1570 (Part 7) 12Cr13H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Stainless Steel category.
GB/T 3280 06Cr19Ni10 is typically used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners., while IS 1570 (Part 7) 12Cr13H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China, while IS 1570 (Part 7) 12Cr13H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, GB/T 3280 06Cr19Ni10 vs IS 1570 (Part 7) 12Cr13H is a 71.9% match.
As per mechanical properties, the match is 20%.
Combined, this makes them a minimal match overall at 54.6%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
GB/T 3280 06Cr19Ni10
IS 1570 (Part 7) 12Cr13H
Tensile Strength
520-720 MPa
470-670 MPa
Yield Strength
205-310 MPa
>=265 MPa (0.2 % proof stress)
Elongation
40-60%
>=20%
Hardness
187 HB max
Not specified
Condition
Not specified
Bars, forgings, plates, A, thickness up to 160 (first row of Table 3)
Typical Applications
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
IS 1570 (Part 7) 12Cr13H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Can GB/T 3280 06Cr19Ni10 Be Substituted With IS 1570 (Part 7) 12Cr13H?
GB/T 3280 06Cr19Ni10 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between GB/T 3280 06Cr19Ni10 and IS 1570 (Part 7) 12Cr13H?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can GB/T 3280 06Cr19Ni10 be substituted with IS 1570 (Part 7) 12Cr13H?
GB/T 3280 06Cr19Ni10 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.