IS 5522 X07Cr17 vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 5522 X07Cr17 (IS 5522:2014) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 5522 X07Cr17 is typically used for utensils, while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. IS 5522 X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 5522 X07Cr17 vs EN 10088-1 1.4006 is a 65.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 5522 X07Cr17:
EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH GOST 5632 06Kh23N28 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
65.6%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 5522 X07Cr17 EN 10088-1 1.4006
Standard IS 5522:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.12 0.08–0.15
Si (%) <=1.00 ≤1.00
Mn (%) <=1.00 ≤1.50
Ni (%) <=0.75 ≤0.75
Cr (%) 16.0-18.0 11.5–13.5
S (%) <=0.030 Not specified
P (%) <=0.040 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 5522 X07Cr17 EN 10088-1 1.4006
Tensile Strength >=450 MPa ≥540 MPa (annealed)
Yield Strength >=205 MPa Not specified
Elongation >=20% ≥18%
Hardness <=183 HB Not specified
Condition Annealed/softened Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
IS 5522 X07Cr17
Utensils
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can IS 5522 X07Cr17 Be Substituted With EN 10088-1 1.4006?
IS 5522 X07Cr17 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 5522 X07Cr17
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 5522 X07Cr17
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 5522 X07Cr17 and EN 10088-1 1.4006?
IS 5522 X07Cr17 specifies S, P which are not specified for EN 10088-1 1.4006.
Can IS 5522 X07Cr17 be substituted with EN 10088-1 1.4006?
IS 5522 X07Cr17 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.