IS 5522 X07Cr17 vs ASTM A959 .-

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 5522 X07Cr17 (IS 5522:2014) and ASTM A959 .- (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 5522 X07Cr17 is typically used for utensils, while ASTM A959 .- is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 5522 X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 .- is defined under ASTM International, originating from United States.

As per chemical composition, IS 5522 X07Cr17 vs ASTM A959 .- is a 74.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 5522 X07Cr17:
EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
74.9%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 5522 X07Cr17 ASTM A959 .-
Standard IS 5522:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.12 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=1.00
Ni (%) <=0.75 <=0.50
Cr (%) 16.0-18.0 18.0-20.0
S (%) <=0.030 <=0.030
P (%) <=0.040 <=0.040
Cb (%) Not specified 0.10-0.60
N (%) Not specified <=0.030
Ti (%) Not specified 0.07-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 5522 X07Cr17 ASTM A959 .-
Tensile Strength >=450 MPa Not specified
Yield Strength >=205 MPa Not specified
Elongation >=20% Not specified
Hardness <=183 HB Not specified
Condition Annealed/softened Not specified
Typical Applications
IS 5522 X07Cr17
Utensils
ASTM A959 .-
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 5522 X07Cr17 Be Substituted With ASTM A959 .-?
IS 5522 X07Cr17 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 5522 X07Cr17
0 active listings and RFQs →
ASTM A959 .-
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 5522 X07Cr17 and ASTM A959 .-?
ASTM A959 .- specifies Cb, N, Ti which are not specified for IS 5522 X07Cr17.
Can IS 5522 X07Cr17 be substituted with ASTM A959 .-?
IS 5522 X07Cr17 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.