EN 10088-1 1.4006 vs ASTM A959 SS410

Close Alternative — 83.3% match based on chemical composition and mechanical property overlap.

EN 10088-1 1.4006 (EN 10088-1:2014) and ASTM A959 SS410 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 1.4006 is typically used for cutlery, turbine blades, fasteners, surgical instruments, while ASTM A959 SS410 is commonly used for cutlery, turbine blades, surgical instruments, fasteners. EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe, while ASTM A959 SS410 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 1.4006 vs ASTM A959 SS410 is a 83.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 83.3%.

Frequently Compared With EN 10088-1 1.4006:
GB/T 3280 06Cr19Ni10 GOST 5632 12Kh13 GOST 5632 08X18H10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4845 EN 10088-1 1.4401 ASTM A959 2205 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 202
Match Breakdown
CHEMISTRY MATCH
83.3%
MECHANICAL MATCH
No shared data
OVERALL
83.3%
Specifications
Property EN 10088-1 1.4006 ASTM A959 SS410
Standard EN 10088-1:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.08–0.15 <=0.15
Si (%) ≤1.00 <=1.00
Mn (%) ≤1.50 <=1.00
Cr (%) 11.5–13.5 11.5-13.5
Ni (%) ≤0.75 Not specified
P (%) Not specified <=0.040
S (%) Not specified <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 1.4006 ASTM A959 SS410
Tensile Strength ≥540 MPa (annealed) Not specified
Hardness HRC 36–45 (hardened) Not specified
Elongation ≥18% Not specified
Typical Applications
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
ASTM A959 SS410
Cutlery, turbine blades, surgical instruments, fasteners
Key Differences
Can EN 10088-1 1.4006 Be Substituted With ASTM A959 SS410?
EN 10088-1 1.4006 and ASTM A959 SS410 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
ASTM A959 SS410
Round Bar → (3 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 2800–3300 mm (110.24–129.92 in)
On M-EX Right Now
EN 10088-1 1.4006
3 active listings and RFQs →
ASTM A959 SS410
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 1.4006 and ASTM A959 SS410?
EN 10088-1 1.4006 specifies Ni which is not specified for ASTM A959 SS410. ASTM A959 SS410 specifies P, S which are not specified for EN 10088-1 1.4006.
Can EN 10088-1 1.4006 be substituted with ASTM A959 SS410?
EN 10088-1 1.4006 and ASTM A959 SS410 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.