Strong Match — 89.8% match
based on chemical composition and mechanical property overlap.
IS 5522 X07Cr17 (IS 5522:2014) and IS 1570 (Part 5) X07Cr17 (IS 1570 (Part 5):1985) are both steel grades.
Both fall under the Stainless Steel category.
IS 5522 X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 5) X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 5522 X07Cr17 vs IS 1570 (Part 5) X07Cr17 is a 97.2% match.
As per mechanical properties, the match is 75%.
Combined, this makes them a strong match overall at 89.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 5522 X07Cr17
IS 1570 (Part 5) X07Cr17
Tensile Strength
>=450 MPa
>=450 MPa
Yield Strength
>=205 MPa
>=205 MPa (0.2 % proof stress)
Elongation
>=20%
>=22.0% (50 mm)
Hardness
<=183 HB
<=183 HB; <=88 HRB
Condition
Annealed/softened
Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Typical Applications
IS 5522 X07Cr17
Utensils
IS 1570 (Part 5) X07Cr17
Not documented
Can IS 5522 X07Cr17 Be Substituted With IS 1570 (Part 5) X07Cr17?
IS 5522 X07Cr17 and IS 1570 (Part 5) X07Cr17 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X07Cr17 is often considered as a substitute for IS 5522 X07Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 5522 X07Cr17 and IS 1570 (Part 5) X07Cr17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 5522 X07Cr17 be substituted with IS 1570 (Part 5) X07Cr17?
IS 5522 X07Cr17 and IS 1570 (Part 5) X07Cr17 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X07Cr17 is often considered as a substitute for IS 5522 X07Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.