SS 14 22 58 2258 vs BS 970 (Part 3) 822M17

Close Alternative — 73.8% match based on chemical composition and mechanical property overlap.

SS 14 22 58 2258 and BS 970 (Part 3) 822M17 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Alloy Steel category. SS 14 22 58 2258 is typically used for heavy duty shafts,gears,aircraft components,crankshafts,forgings,highly stressed bolts, while BS 970 (Part 3) 822M17 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy case hardening steel (table 15). SS 14 22 58 2258 is defined under Swedish Standards (SS), originating from Sweden, while BS 970 (Part 3) 822M17 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, SS 14 22 58 2258 vs BS 970 (Part 3) 822M17 is a 73.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 73.8%.

Frequently Compared With SS 14 22 58 2258:
NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A IS 4367 10Cr9Mo10 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
73.8%
MECHANICAL MATCH
No shared data
OVERALL
73.8%
Specifications
Property SS 14 22 58 2258 BS 970 (Part 3) 822M17
Standard SS 14 22 58 BS 970 (Part 3):1991
Category Alloy Steel Alloy Steel
C (%) 0.30-0.38 0.14-0.20
Si (%) <=0.40 0.10-0.40
Mn (%) 0.50-0.80 0.40-0.70
P (%) <=0.025 <=0.04
S (%) <=0.035 <=0.05
Cr (%) 1.30-1.70 1.30-1.70
Mo (%) 0.15-0.30 0.15-0.25
Ni (%) 1.30-1.70 1.75-2.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SS 14 22 58 2258 BS 970 (Part 3) 822M17
Tensile Strength 900-1100 MPa Not specified
Yield Strength 700-900 MPa Not specified
Elongation 11-14 % Not specified
Hardness 260-320 HB Not specified
Typical Applications
SS 14 22 58 2258
heavy duty shafts,gears,aircraft components,crankshafts,forgings,highly stressed bolts
BS 970 (Part 3) 822M17
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy case hardening steel (Table 15)
Can SS 14 22 58 2258 Be Substituted With BS 970 (Part 3) 822M17?
SS 14 22 58 2258 and BS 970 (Part 3) 822M17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
SS 14 22 58 2258
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6500–6500 mm (255.91–255.91 in)
BS 970 (Part 3) 822M17
No active listings currently.
On M-EX Right Now
SS 14 22 58 2258
2 active listings and RFQs →
BS 970 (Part 3) 822M17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between SS 14 22 58 2258 and BS 970 (Part 3) 822M17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can SS 14 22 58 2258 be substituted with BS 970 (Part 3) 822M17?
SS 14 22 58 2258 and BS 970 (Part 3) 822M17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.