Post Stock Login Register

SS 14 22 58 2258 vs IS 1570 (Part 7) 10Cr36Mo10H

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

SS 14 22 58 2258 and IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Alloy Steel category. SS 14 22 58 2258 is typically used for heavy duty shafts,gears,aircraft components,crankshafts,forgings,highly stressed bolts, while IS 1570 (Part 7) 10Cr36Mo10H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. SS 14 22 58 2258 is defined under Swedish Standards (SS), originating from Sweden, while IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, SS 14 22 58 2258 vs IS 1570 (Part 7) 10Cr36Mo10H is a 54.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With SS 14 22 58 2258:
NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 103Cr6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 07Cr4Mo6 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
54.8%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property SS 14 22 58 2258 IS 1570 (Part 7) 10Cr36Mo10H
Standard SS 14 22 58 IS 1570 (Part 7):1992
Category Alloy Steel Alloy Steel
C (%) 0.30-0.38 <=0.15
Si (%) <=0.40 0.25-1.0
Mn (%) 0.50-0.80 0.30-0.60
P (%) <=0.025 <=0.040
S (%) <=0.035 <=0.030
Cr (%) 1.30-1.70 8.00-10.00
Mo (%) 0.15-0.30 0.90-1.10
Ni (%) 1.30-1.70 Not specified
Al (metallic) (%) Not specified <=0.02
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SS 14 22 58 2258 IS 1570 (Part 7) 10Cr36Mo10H
Tensile Strength 900-1100 MPa 410-560 MPa
Yield Strength 700-900 MPa >=135 MPa (0.2 % proof stress)
Elongation 11-14 % >=20%
Hardness 260-320 HB Not specified
Condition Not specified Pipes, A, thickness - (first row of Table 3)
Typical Applications
SS 14 22 58 2258
heavy duty shafts,gears,aircraft components,crankshafts,forgings,highly stressed bolts
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can SS 14 22 58 2258 Be Substituted With IS 1570 (Part 7) 10Cr36Mo10H?
SS 14 22 58 2258 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
SS 14 22 58 2258
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6500–6500 mm (255.91–255.91 in)
IS 1570 (Part 7) 10Cr36Mo10H
No active listings currently.
On M-EX Right Now
SS 14 22 58 2258
2 active listings and RFQs →
IS 1570 (Part 7) 10Cr36Mo10H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between SS 14 22 58 2258 and IS 1570 (Part 7) 10Cr36Mo10H?
SS 14 22 58 2258 specifies Ni which is not specified for IS 1570 (Part 7) 10Cr36Mo10H. IS 1570 (Part 7) 10Cr36Mo10H specifies Al (metallic) which is not specified for SS 14 22 58 2258.
Can SS 14 22 58 2258 be substituted with IS 1570 (Part 7) 10Cr36Mo10H?
SS 14 22 58 2258 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.