SS 14 22 58 2258 vs IS 4367 10Cr9Mo10

Minimal Match — 40.6% match based on chemical composition and mechanical property overlap.

SS 14 22 58 2258 and IS 4367 10Cr9Mo10 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. SS 14 22 58 2258 is defined under Swedish Standards (SS), originating from Sweden, while IS 4367 10Cr9Mo10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, SS 14 22 58 2258 vs IS 4367 10Cr9Mo10 is a 60.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 40.6%.

Frequently Compared With SS 14 22 58 2258:
NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 103Cr6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
60.9%
MECHANICAL MATCH
0%
OVERALL
40.6%
Specifications
Property SS 14 22 58 2258 IS 4367 10Cr9Mo10
Standard SS 14 22 58 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.30-0.38 <=0.15
Si (%) <=0.40 <=0.50
Mn (%) 0.50-0.80 0.40-0.70
P (%) <=0.025 <=0.035
S (%) <=0.035 <=0.035
Cr (%) 1.30-1.70 2.00-2.50
Mo (%) 0.15-0.30 0.90-1.10
Ni (%) 1.30-1.70 <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SS 14 22 58 2258 IS 4367 10Cr9Mo10
Tensile Strength 900-1100 MPa 410-590 MPa
Yield Strength 700-900 MPa 245 MPa min
Elongation 11-14 % >=18%
Hardness 260-320 HB Not specified
Izod Impact Not specified 55 J min
Hardness (soft annealed) Not specified <=187 HB
Condition Not specified Normalised and tempered, ruling section up to 50 mm
Typical Applications
SS 14 22 58 2258
heavy duty shafts,gears,aircraft components,crankshafts,forgings,highly stressed bolts
IS 4367 10Cr9Mo10
Not documented
Can SS 14 22 58 2258 Be Substituted With IS 4367 10Cr9Mo10?
SS 14 22 58 2258 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
SS 14 22 58 2258
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6500–6500 mm (255.91–255.91 in)
IS 4367 10Cr9Mo10
No active listings currently.
On M-EX Right Now
SS 14 22 58 2258
2 active listings and RFQs →
IS 4367 10Cr9Mo10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between SS 14 22 58 2258 and IS 4367 10Cr9Mo10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can SS 14 22 58 2258 be substituted with IS 4367 10Cr9Mo10?
SS 14 22 58 2258 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.