SS 14 22 58 2258 vs EN 10028-2 10CrMo9-10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

SS 14 22 58 2258 and EN 10028-2 10CrMo9-10 (EN 10028-2:2017) are both steel grades. Both fall under the Alloy Steel category. SS 14 22 58 2258 is typically used for heavy duty shafts,gears,aircraft components,crankshafts,forgings,highly stressed bolts, while EN 10028-2 10CrMo9-10 is commonly used for flat products for pressure purposes. SS 14 22 58 2258 is defined under Swedish Standards (SS), originating from Sweden, while EN 10028-2 10CrMo9-10 is defined under European Standard (EN), originating from Europe.

As per chemical composition, SS 14 22 58 2258 vs EN 10028-2 10CrMo9-10 is a 56% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With SS 14 22 58 2258:
NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A IS 4367 10Cr9Mo10 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
56%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property SS 14 22 58 2258 EN 10028-2 10CrMo9-10
Standard SS 14 22 58 EN 10028-2:2017
Category Alloy Steel Alloy Steel
C (%) 0.30-0.38 0.08-0.14
Si (%) <=0.40 <=0.50
Mn (%) 0.50-0.80 0.40-0.80
P (%) <=0.025 <=0.020
S (%) <=0.035 <=0.010
Cr (%) 1.30-1.70 2.00-2.50
Mo (%) 0.15-0.30 0.90-1.10
Ni (%) 1.30-1.70 Not specified
N (%) Not specified <=0.012
Cu (%) Not specified <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SS 14 22 58 2258 EN 10028-2 10CrMo9-10
Tensile Strength 900-1100 MPa 480-630 MPa
Yield Strength 700-900 MPa >=310 MPa
Elongation 11-14 % >=18%
Hardness 260-320 HB Not specified
Condition Not specified Usual delivery condition normalized and tempered (+NT), nominal thickness up to 16 mm; transverse direction, Yield Strength is ReH, Elongation is A
Typical Applications
SS 14 22 58 2258
heavy duty shafts,gears,aircraft components,crankshafts,forgings,highly stressed bolts
EN 10028-2 10CrMo9-10
Flat products for pressure purposes
Key Differences
Can SS 14 22 58 2258 Be Substituted With EN 10028-2 10CrMo9-10?
SS 14 22 58 2258 and EN 10028-2 10CrMo9-10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
SS 14 22 58 2258
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6500–6500 mm (255.91–255.91 in)
EN 10028-2 10CrMo9-10
No active listings currently.
On M-EX Right Now
SS 14 22 58 2258
2 active listings and RFQs →
EN 10028-2 10CrMo9-10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between SS 14 22 58 2258 and EN 10028-2 10CrMo9-10?
SS 14 22 58 2258 specifies Ni which is not specified for EN 10028-2 10CrMo9-10. EN 10028-2 10CrMo9-10 specifies N, Cu which are not specified for SS 14 22 58 2258.
Can SS 14 22 58 2258 be substituted with EN 10028-2 10CrMo9-10?
SS 14 22 58 2258 and EN 10028-2 10CrMo9-10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.